TEST REPORT OF CAUSTIC POTASH FLAKES |
Flakes
|
| 1. Assay |
min |
88.0% |
| 2. Carbonate as K2Co3 |
max |
0.5% |
| 3. Chlorides as Kcl |
max |
0.05% |
| 4.Iron as Fe |
max |
0.003% |
| 5.Sodium |
max |
0.6% |
|
|
POTASSIUM CARBONATE |
|
PRODUCT SPECIFICATION
|
| Potassium Carbonate (Powder) |
K2CO3 |
MW : 138 |
CP |
| PARTICULARS |
|
| 1. Appearance |
Fine White powder |
| 2. Identification |
Positive |
| 3. Free alkali, as KOH |
0.2 |
% |
(max) (w/w) |
| 4. Chloride, as Cl /td>
| 50 |
ppm |
(max) |
| 5. Arsenic, as As |
Not traceable |
| 6. Iron, as Fe |
10 |
ppm |
(max) |
| 7. Heavy Metals, as Pb |
5 |
ppm |
(max) |
| 8. Assay, as K2SO4, on dried basis |
99.0 |
% |
(min) ( w/w) |
| 9. Particle size analysis |
|
Materials passing through 100
BSS mesh are |
96.0 |
% |
(min) (w/w) |
|
| |
| CALCIUM HYPOCHLORITE – 65% & 70% GRANULAR & TABLET |
| |
SPECIFICATION
|
| PARAMETERS |
CALCIUM HYPOCHLORITE-65% MIN. GRANULAR & TABLET. |
CALCIUM HYPOCHLORITE-70% MIN. GRANULAR & TABLET. |
|
STANDARD |
TYPICAL |
STANDARD |
TYPICAL |
| CA (OCL2) |
65.00% MIN. |
64.48% |
70.00% MIN. |
71.46% |
| CA (OH)2 |
4.00% MAX. |
2.12% |
2.00% MAX. |
1.52% |
| CA CO3 |
4.00% MAX. |
4.71% |
3.00% MAX. |
2.42% |
| CACL2 |
3.50% MAX. |
2.46% |
5.10% MAX. |
3.66% |
| NACL |
16.00% MAX. |
16.36% |
14.00% MAX. |
7.28% |
| CA(CL03)2 |
0.25% MAX. |
0.21% |
0.25% MAX. |
0.22% |
| MOISTURE & OTHERS |
5.10% |
7.66% |
5-10% |
13.38% |
|
| |
GRANULAR MESH & DENSITY
|
| BULK DENSITY |
1.1% G/CC |
1.14% G/CC |
1.1% G/CC |
1.14% G/CC |
| MATERIAL PASSING THROUGH 100 BSS SEIVE |
1.5% MAX. |
|
| |
|
|
TABLET WEIGHTS & DIMENSIONS
|
| TABLET WEIGHT |
DIAMETER |
THICKNESS |
| 0.5 GRAMS |
10 MM |
4 MM |
| 7 GRAMS |
24 MM |
9 MM |
| 20 GRAMS |
30 MM |
20 MM |
| 100 GRAMS |
63.5 MM |
20 MM |
|
| |
|
|
SPECIFICATION OF CHLORO SULPHONIC ACID
|
| S.NO. |
CHARACTERISTICS |
SPECIFICATIONS |
| 01 |
Purity (as CISO2-OH)% by mass |
96% min. |
| 02. |
Free Sulphuric Acid (as H2SO4) % By mass |
3.0 Max. |
| 03. |
Free SO3/Hcl % by mass |
2.0 Max. |
|
| |